Fotoactivación de nanotubos de dióxido de titanio inducida por luz uv

ATALIA GOMEZ CORTEZ

RESUMEN En este trabajo se sintetizaron fotocatalizadores de Ti / TiO2 mediante la anodización electroquímica de la lámina y malla de Ti. Los nanotubos de Ti / TiO2 (NT Ti / TiO2) se sintetizaron mediante anodización electroquímica mediante un electrolito de 0.3 % p/p NH4F + 3 % agua destilada+ etilenglicol durante 15 y 30 min de anodizado para ambas muestras, posteriormente fueron sometidas a un tratamiento térmico a 450 °C con flujo continuo de aire durante 2 h. Con el fin de comparar la fotorespuesta que presentan los nanotubos de Ti / TiO2 cuando son sometidos a luz UV a diferentes pH. Los fotocatalizadores fueron sometidos a microscopia electrónica de barrido para observar la morfología y difracción de rayos X para en la cual se identificó las fases cristalinas. Para evaluar la fotoactividad de los fotocatalizadores se utilizó una celda electroquímica de tres electrodos, posteriormente se evaluó su desempeño mediante la remoción del colorante verde ácido 50 a pH 1,7 y 10 Los mejores resultados se obtuvieron a pH ácido usando los NT Ti / TiO2 obtenidos mediante la anodización de la lámina durante 15 min donde los nanotubos se formaron más uniformes y con mejor ordenamiento presentando un diámetro de poro de 100.8 nm además la formación de la fase anatasa en la lámina de 15 min es más cristalina, esto es favorable ya que presenta una mayor densidad de corriente y el comportamiento fotocatalítico es mayor en comparación con las demás muestras. La eficiencia de remoción del colorante verde ácido 50 fue de 48.09 % en 2 h para la lámina anodizada durante 15 min a pH ácido.

ABSTRACT In this work Ti / TiO2 photocatalysts were synthesized by electrochemical anodization of the Ti foil and mesh. The Ti / TiO2 nanotubes (NT Ti / TiO2) were synthesized by electrochemical anodization using an electrolyte of 0.3% w / w NH4F + 3% distilled water + ethylene glycol during 15 and 30 min of anodization for both samples, afterwards they were subjected to a treatment thermal at 450 ° C with continuous air flow for 2 h. In order to compare the photoresist presented by the Ti / TiO2 nanotubes when they are subjected to UV light at different pH. The photocatalysts were subjected to scanning electron microscopy to observe the morphology and X-ray diffraction for which the crystalline phases were identified. To evaluate the photoactivity of the photocatalysts, a three electrodes electrochemical cell was used, after which its performance was evaluated by removing acid green dye 50 at pH 1, 7 and 10. The best results were obtained at acid pH using NT Ti / TiO2 obtained by anodizing the sheet during 15 min where the nanotubes were formed more uniform and with better ordering, having a pore diameter of 100.8 nm plus the formation of the anatase phase in the 15 min sheet it is more crystalline, this is favorable since it has a higher current density and the photocatalytic behavior is higher compared to the other samples. The removal efficiency of acid green dye 50 was 48.09% in 2 h for the anodized sheet during 15 min at acid pH.

Tipo de documento: Tesis de maestría

Formato: Adobe PDF

Audiencia: Investigadores

Idioma: Español

Área de conocimiento: INGENIERÍA Y TECNOLOGÍA

Campo disciplinar: CIENCIAS TECNOLÓGICAS

Nivel de acceso: Acceso Abierto