| dc.description | Resumen.
El magnesio (Mg) es uno de los materiales más prometedores debido a su ligereza
ya que actualmente es utilizado para aplicaciones de bioingeniería. El Mg posee
una serie de características atractivas que hacen que los materiales a base de Mg
sean potencialmente utilizados para aplicaciones en la industria médica debido a su
buena biocompatibilidad y biodegradabilidad.
En este trabajo, se sintetizaron aleaciones ternarias de Mg-Zn-Ca, mediante
molienda mecánica (MM). El objetivo de este trabajo fue la evaluación del efecto
citotóxico de las aleaciones base Mg producidas por MM, así como el efecto del
tiempo de molienda en sus propiedades microestructurales, las aleaciones base Mg
se sintetizaron en un molino planetario bajo atmósfera de argón usando un
recipiente y balines de acero inoxidable. El proceso de molienda se llevó a cabo a
400 rpm durante varios tiempos de molienda 2, 5, 10,15 y 20 h. El análisis de
refinamiento de los patrones de difracción de rayos X muestra la presencia de la
fase MgZn. Los resultados mostraron que es posible obtener aleaciones mediante
MM, los polvos obtenidos por MM en diferentes tiempos se caracterizaron por
microscopía electrónica de barrido (MEB) y difracción de rayos X (DRX). Los
ensayos de microdureza Vickers (Hv) se realizaron aplicando una carga de
indentación de 200 g. La citotoxicidad es muy importante para determinar algún
efecto tóxico de las aleaciones base Mg, las pruebas citotóxicas se llevaron a cabo
por el método de Sulforodamina B (SRB) el cual reveló que las aleaciones de
Mg65%Zn30%Ca5% y Mg70%Zn25%Ca5% no inducían toxicidad en las células. | es_MX |
| dc.description | Abstract
Magnesium (Mg) is one of the most promising materials due to its lightness
and because it is currently used for bioengineering applications. Mg possesses a
number of attractive characteristics that make Mg-based materials potentially used
for applications in the medical industry due to its good biocompatibility and
biodegradability.
In this work, ternary alloys of Mg-Zn-Ca were synthesized by mechanical milling
(Mm). The objective of this work was the evaluation of the cytotoxic effect of the Mg
base alloys produced by MM, as well as the effect of the milling time on their
microstructural properties, the Mg base alloys were synthesized in a planetary mill
under argon atmosphere using a container stainless steel and balls. The milling
process was carried out at 400 rpm for various millin times 2, 5, 10, 15 and 20 hours.
The refinement analysis of the X-ray diffraction patterns shows the presence of the
MgZn phase. The results showed that it is possible to obtain alloys by MM, the
alloyed powders obtained by MM at different times were characterized by scanning
electron microscopy (SEM) and X-ray diffraction (XRD). The Vickers microhardness
tests (Hv) were carried out by applying an indentation load of 200 gr. Cytotoxicity is
very important to determine some toxic effect of Mg base alloys, cytotoxic tests were
carried out by the Sulforhodamine B (SRB) method which revealed that Mg65%
Zn30% Ca5% and Mg70% Zn25%Ca5% alloys did not induce toxicity in the cells. | es_MX |
| dc.format | pdf - Adobe PDF | es_MX |
| dc.language | spa - Español | es_MX |
| dc.publisher | Autor | es_MX |
| dc.rights | openAccess - Acceso Abierto | es_MX |
| dc.subject | 7 - INGENIERÍA Y TECNOLOGÍA | es_MX |
| dc.subject.other | 33 - CIENCIAS TECNOLÓGICAS | es_MX |
| dc.title | Mecanosíntesis de biomateriales base magnesio Mg, mediante molienda mecánica MM | es_MX |
| dc.type | doctoralThesis - Tesis de doctorado | es_MX |
| uaem.unidad | Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) - Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) | es_MX |
| uaem.programa | Doctorado en Ciencias - Doctorado en Ciencias | es_MX |
| dc.type.publication | acceptedVersion | es_MX |
| dc.audience | researchers - Investigadores | es_MX |
| dc.date.received | 2022-01-25 | |