Evaluación en la corrosión y protección del acero de refuerzo embebidas de concreto en presencia de grafito y su instituto de investigación en ciencias básicas y aplicadas aplicadas efecto en las propiedades mecánicaselectroquímicas
| dc.rights.license | http://creativecommons.org/licenses/by-nc/4.0 - Atribución-NoComercial | es_MX |
| dc.contributor | Jorge Uruchurtu Chavarín | es_MX |
| dc.contributor.author | ALEJANDRO FLORES NICOLÁS | es_MX |
| dc.contributor.other | director - Director | es_MX |
| dc.coverage.spatial | MEX - México | es_MX |
| dc.date | 2020-11-19 | |
| dc.date.accessioned | 2021-05-26T17:59:37Z | |
| dc.date.available | 2021-05-26T17:59:37Z | |
| dc.identifier.uri | http://riaa.uaem.mx/handle/20.500.12055/1554 | |
| dc.description | RESUMEN En esta presente investigación se estudió el uso del material de carbono en su forma alotrópica de grafito, como adición en el concreto reforzado, evaluando su efecto en las propiedades físicas y electroquímicas. Se elaboraron 4 diferentes calidades de concreto reforzado, con porcentaje de grafito 2.5 %, 7.5% y 15 % como sustitución parcial del cemento, para su evaluación en la resistencia a la compresión y su resistencia a la corrosión del acero de refuerzo. Se realizaron las pruebas físicas de los materiales de volumétrico seco y suelto, peso volumétrico seco compacto, granulometría del agregado, densidad y absorción. Al concreto recién mezclado se realizaron las pruebas físicas como: revenimiento, temperatura, masa unitaria, contenido de aire. En las pruebas de resistencia a compresión (F´c) los especímenes se curaron a 28 días y se ensayaron durante 7, 14 y 28 inmersas en una solución de cloruro de sodio (NaCl) al 3 %, simulando un ambiente agresivo, durante 168 días de exposición. Se realizaron las técnicas electroquímicas como: potencial de media celda (H.C.P.), ruido electroquímico (E.N.) y resistencia a la polarización lineal (R.P.L.). Asimismo, se estudiaron los componentes químicos de la pasta de concreto; empleando barrido (M.E.B.). Se observó que las muestras con adición de 2.5 % y 7.5% de grafito obtuvieron un F´c mayor comparado con la muestra control. Se apreciaron cloruros dentro de la matriz del concreto derivado de la contaminación de los agregados, afectando las propiedades electroquímicas del acero. En las técnicas electroquímicas, todas las muestras con y sin adición de grafito, adquirieron valores muy negativos de potencial de corrosión, y bajos valores de resistencia al ruido electroquímico (Rn) y resistencia a la polarización lineal (Rp), demostrando alta corrosión en el metal. | es_MX |
| dc.description | ABSTRACT In this present investigation, the use of carbon material in its allotropic form of graphite was studied, as an addition to reinforced concrete, evaluating its effect on the physical and electrochemical properties. Four different qualities of reinforced concrete were made, with 2.5%, 7.5% and 15% graphite percentage as partial cement replacement, for evaluation of compression resistance and and its resistance to corrosion of reinforcing steel. Physical tests of fine aggregate and coarse aggregate materials were performed for your mix design as; loose and dry volumetric weights, compact dry volumetric weights, aggregate granulometry, density and absorption. To the recently mixed concrete the physical tests were used as; slump, temperature, unit mass, air content. In the compression resistence (F´c) tests, the samples were cured at 28 days and tested for 7, 14, and 28 days. In electrochemical tests the samples were exposed in a 3% sodium chloride (NaCl) solution, simulating an aggressive environment, during 168 days. Different electrochemical techniques were performed such as: half-cell potential (H.C.P.), electrochemical noise (E.N.), and linear polarization resistance (L.P.R.), the chemical components of the concrete paste were also studied; using the techniques of X-ray diffraction (X.R.D.) and scanning electron microscope (S.E.M.). It was observed that the sample with the addition of 2.5% and 7.5% graphite obtained a higher F´c compared to the control simple. Chlorides were appreciated at the start of the concrete paste, derived from the contamination of the aggregates, affecting the electrochemical properties of steel. On the electrochemical properties with the additions of graphite, acquired very negative corrosion potential values, and low values of resistance to electrochemical noise (Rn), and resistance to linear polarization (Rp), demonstrating high corrosion in the metal. | es_MX |
| dc.format | pdf - Adobe PDF | es_MX |
| dc.language | spa - Español | es_MX |
| dc.publisher | El autor | es_MX |
| dc.rights | openAccess - Acceso Abierto | es_MX |
| dc.subject | 7 - INGENIERÍA Y TECNOLOGÍA | es_MX |
| dc.subject.other | 33 - CIENCIAS TECNOLÓGICAS | es_MX |
| dc.title | Evaluación en la corrosión y protección del acero de refuerzo embebidas de concreto en presencia de grafito y su instituto de investigación en ciencias básicas y aplicadas aplicadas efecto en las propiedades mecánicaselectroquímicas | es_MX |
| dc.type | masterThesis - Tesis de maestría | es_MX |
| uaem.unidad | Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) - Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) | es_MX |
| uaem.programa | Maestría en Ingeniería y Ciencias Aplicadas - Maestría en Ingeniería y Ciencias Aplicadas | es_MX |
| dc.type.publication | acceptedVersion | es_MX |
| dc.audience | researchers - Investigadores | es_MX |
Ficheros en el recurso
Este recurso aparece en la(s) siguiente(s) colección(ones)
-
Colección Tesis Posgrado
Se trata de tesis realizadas por estudiantes egresados de programas de posgrado de nuestra institución.