| dc.rights.license | http://creativecommons.org/licenses/by-nc/4.0 - Atribución-NoComercial | es_MX |
| dc.contributor | Jorge Uruchurtu Chavarín | es_MX |
| dc.contributor.author | ALEJANDRO FLORES NICOLÁS | es_MX |
| dc.contributor.other | director - Director | es_MX |
| dc.coverage.spatial | MEX - México | es_MX |
| dc.date | 2020-11-19 | |
| dc.date.accessioned | 2021-05-26T17:59:37Z | |
| dc.date.available | 2021-05-26T17:59:37Z | |
| dc.identifier.uri | http://riaa.uaem.mx/handle/20.500.12055/1554 | |
| dc.description | RESUMEN
En esta presente investigación se estudió el uso del material de carbono en
su forma alotrópica de grafito, como adición en el concreto reforzado,
evaluando su efecto en las propiedades físicas y electroquímicas.
Se elaboraron 4 diferentes calidades de concreto reforzado, con porcentaje
de grafito 2.5 %, 7.5% y 15 % como sustitución parcial del cemento, para su
evaluación en la resistencia a la compresión y su resistencia a la corrosión
del acero de refuerzo. Se realizaron las pruebas físicas de los materiales de
volumétrico seco y suelto, peso volumétrico seco compacto, granulometría
del agregado, densidad y absorción. Al concreto recién mezclado se
realizaron las pruebas físicas como: revenimiento, temperatura, masa
unitaria, contenido de aire. En las pruebas de resistencia a compresión (F´c)
los especímenes se curaron a 28 días y se ensayaron durante 7, 14 y 28
inmersas en una solución de cloruro de sodio (NaCl) al 3 %, simulando un
ambiente agresivo, durante 168 días de exposición. Se realizaron las
técnicas electroquímicas como: potencial de media celda (H.C.P.), ruido
electroquímico (E.N.) y resistencia a la polarización lineal (R.P.L.). Asimismo,
se estudiaron los componentes químicos de la pasta de concreto; empleando
barrido (M.E.B.). Se observó que las muestras con adición de 2.5 % y 7.5%
de grafito obtuvieron un F´c mayor comparado con la muestra control. Se
apreciaron cloruros dentro de la matriz del concreto derivado de la
contaminación de los agregados, afectando las propiedades electroquímicas
del acero. En las técnicas electroquímicas, todas las muestras con y sin
adición de grafito, adquirieron valores muy negativos de potencial de
corrosión, y bajos valores de resistencia al ruido electroquímico (Rn) y
resistencia a la polarización lineal (Rp), demostrando alta corrosión en el metal. | es_MX |
| dc.description | ABSTRACT
In this present investigation, the use of carbon material in its allotropic form of
graphite was studied, as an addition to reinforced concrete, evaluating its
effect on the physical and electrochemical properties. Four different qualities
of reinforced concrete were made, with 2.5%, 7.5% and 15% graphite
percentage as partial cement replacement, for evaluation of compression
resistance and and its resistance to corrosion of reinforcing steel. Physical
tests of fine aggregate and coarse aggregate materials were performed for
your mix design as; loose and dry volumetric weights, compact dry volumetric
weights, aggregate granulometry, density and absorption. To the recently
mixed concrete the physical tests were used as; slump, temperature, unit
mass, air content. In the compression resistence (F´c) tests, the samples
were cured at 28 days and tested for 7, 14, and 28 days. In electrochemical
tests the samples were exposed in a 3% sodium chloride (NaCl) solution,
simulating an aggressive environment, during 168 days. Different
electrochemical techniques were performed such as: half-cell potential
(H.C.P.), electrochemical noise (E.N.), and linear polarization resistance
(L.P.R.), the chemical components of the concrete paste were also studied;
using the techniques of X-ray diffraction (X.R.D.) and scanning electron
microscope (S.E.M.). It was observed that the sample with the addition of
2.5% and 7.5% graphite obtained a higher F´c compared to the control
simple. Chlorides were appreciated at the start of the concrete paste, derived
from the contamination of the aggregates, affecting the electrochemical
properties of steel. On the electrochemical properties with the additions of
graphite, acquired very negative corrosion potential values, and low values of
resistance to electrochemical noise (Rn), and resistance to linear polarization
(Rp), demonstrating high corrosion in the metal. | es_MX |
| dc.format | pdf - Adobe PDF | es_MX |
| dc.language | spa - Español | es_MX |
| dc.publisher | El autor | es_MX |
| dc.rights | openAccess - Acceso Abierto | es_MX |
| dc.subject | 7 - INGENIERÍA Y TECNOLOGÍA | es_MX |
| dc.subject.other | 33 - CIENCIAS TECNOLÓGICAS | es_MX |
| dc.title | Evaluación en la corrosión y protección del acero de refuerzo embebidas de concreto en presencia de grafito y su instituto de investigación en ciencias básicas y aplicadas aplicadas efecto en las propiedades mecánicaselectroquímicas | es_MX |
| dc.type | masterThesis - Tesis de maestría | es_MX |
| uaem.unidad | Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) - Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) | es_MX |
| uaem.programa | Maestría en Ingeniería y Ciencias Aplicadas - Maestría en Ingeniería y Ciencias Aplicadas | es_MX |
| dc.type.publication | acceptedVersion | es_MX |
| dc.audience | researchers - Investigadores | es_MX |