| dc.description | RESUMEN
En este trabajo se llevó a cabo el estudio de degradación del colorante textil
azul terasil (AT) mediante los procesos de fotocatálisis y electrofotocatálisis,
utilizando nanotubos de TiO2 como electrodo de trabajo dopados con diferente
cantidad de Rutenio (0, 0.005, 0.02, 0.04, 0.08, 0.1 y 0.15%w) iluminados con
luz UV y luz visible ambos procesos. Los nanotubos de TiO2 (NT TiO2) se
obtuvieron mediante la técnica convencional de anodización (en una solución
no acuosa que contenía 0.5%w NH4F, 10%w H2O y el resto etilenglicol), se les
dio un tratamiento térmico de 600°C para priorizar la formación de la fase
anatasa, posteriormente los sustratos fueron dopados con diferentes
cantidades de RuCl3 por el método de impregnación y fueron calcinados a
200°C, durante 2 horas.
La degradación del colorante textil conocido como AT, se llevó a cabo durante
120 min, a temperatura ambiente durante 2 horas. Los efectos de la
degradación del colorante AT se midieron mediante la absorción (UV- Vis) de
la muestra cada 15 min. Se obtuvo una máxima eficiencia de degradación
usando el electrodo con 0.15wt %Ru de 98% usando luz UV y 55% con luz vis,
mediante el proceso de electrofotocatálisis, por otro lado, se alcanzó 83% (luz
UV) y 38% (luz Vis) por fotocatálisis.
Los NT TiO2 dopados con Rutenio, fueron estudiados utilizando las técnicas
de caracterización: Difracción de Rayos X, RAMAN, Microscopía de Barrido,
SEM-EDS y LSV.
Por otro lado, se llevó a cabo la determinación electroquímica de la demanda
Química de Oxígeno, utilizando los NT TiO2 reducidos mediante la aplicación
de una corriente de -5mA durante 10 min, se utilizaron ftalato de Potasio
(KHP), ácido acético (CH3COOH) y glucosa (C6H12O6) como contaminantes
modelo para la determinación de la carga Q y así determinar la DQO. | es_MX |
| dc.description | ABSTRACT
In this work, the degradation study of terasil blue textile dye was carried out
through photocatalysis and electrophotocatalysis processes, using TiO2
nanotubes as a working electrode doped with different amounts of Ruthenium
(0, 0.005, 0.02, 0.04, 0.08, 0.1 and 0.15% w) illuminated with UV light and
visible light both processes. The TiO2 (NT TiO2) nanotubes were obtained
using the conventional anodization technique by means of (in a non-aqueous
solution containing 0.5% w NH4F, 10% w H2O and the rest ethylene glycol),
they were given a heat treatment of 600 °C to prioritize the formation of the
anatase phase, then the substrates were doped with different amounts of RuCl3
by the impregnation method and were calcined at 200 °C, for 2 hours.
The degradation of the textile dye known as terasil blue during 120 min, at room
temperature for 2 hours. The degradation effects of the terasil blue dye were
measured by absorption (UV-Vis) of the sample every 15 min. Maximum
degradation efficiency was obtained using the electrode with 0.15wt. % Ru was
98% using UV light and 55% with vis light, through the electrophotocatalysis
process, on the other hand, 83% (UV light) and 38% (Vis light) by
photocatalysis.
The ruthenium doped nanotubes of TiO2 were studied using the
characterization techniques: X-Ray Diffraction, RAMAN, Scanning Microscopy
SEM-EDS and LSV.
On the other hand, the electrochemical determination of the Chemical Oxygen
demand was carried out using the nanotubes of TiO2 reduced by applying a
current of -5mA for 10 min, potassium phthalate (KHP), acetic acid (CH3COOH)
were used and glucose (C6H12O6) as model contaminants for the determination
of the charge Q to determine the COD. | es_MX |
| dc.format | pdf - Adobe PDF | es_MX |
| dc.language | spa - Español | es_MX |
| dc.publisher | autor | es_MX |
| dc.rights | openAccess - Acceso Abierto | es_MX |
| dc.subject | 7 - INGENIERÍA Y TECNOLOGÍA | es_MX |
| dc.subject.other | 33 - CIENCIAS TECNOLÓGICAS | es_MX |
| dc.title | Influencia del rutenio en la oxidación fotoelectrocatalítica del colorante textil azul terazil utilizando un fotoanodo de matriz de nanotubos de TiO2 iluminado con luz uv y luz visible | es_MX |
| dc.type | doctoralThesis - Tesis de doctorado | es_MX |
| uaem.unidad | Centro de Investigación en Ingeniería y Ciencias Aplicadas (CIICAP) - Centro de Investigación en Ingeniería y Ciencias Aplicadas (CIICAP) | es_MX |
| uaem.programa | Doctorado en Ciencias - Doctorado en Ciencias | es_MX |
| dc.type.publication | acceptedVersion | es_MX |