| dc.rights.license | http://creativecommons.org/licenses/by-nc/4.0 - Atribución-NoComercial | es_MX |
| dc.contributor | MARISOL GUIZADO RODRIGUEZ | es_MX |
| dc.contributor.author | PARIS JONATHAN REYNOSO GARCIA | es_MX |
| dc.contributor.other | director - Director | es_MX |
| dc.coverage.spatial | MEX - México | es_MX |
| dc.date | 2021-03-02 | |
| dc.date.accessioned | 2021-04-15T02:00:27Z | |
| dc.date.available | 2021-04-15T02:00:27Z | |
| dc.identifier.uri | http://riaa.uaem.mx/handle/20.500.12055/1450 | |
| dc.description | RESUMEN
Este proyecto presenta la obtención de nanopartículas (Np´s) de plata de
morfología esférica de 12.7 ± 1.2 nm de diámetro y, triangular de 28.9 ± 0.8 nm
por cada lado de los triángulos; además se observaron nanotriángulos menores a
5 nm.
La estabilidad de las Np´s se logró utilizando el ditiocarbamato (DTC): 4-
(etilaminoditiocarbamato) metilpiridina di-n-butilestaño (IV) con una concentración
de 8.69×10-3 mM. El análisis óptico UV-vis de las Np´s mostró una longitud de
onda de 390 nm, característica para la morfología esférica y, dos señales a 331 y
754 nm para la morfología triangular; con lo anterior se corroboró cada morfología
indicada. Los espectros UV-vis mostraron la estabilidad de las Np´s con el DTC
por más de tres meses.
Se obtuvieron las Np´s de los copolímeros basados en 3-hexiltiofeno con 2-(tiofen3-il) acetato de 2-(etil(4-(4-nitroestiril)fenil)amino)etilo (PI) y 3-hexiltiofeno con 2-
(tiofen-3-il) acetato de (E)-2-(etil(4-((4-nitrofenil)diazenil)fenil)amino)etilo (PA),
disolviéndolas en diferentes relaciones de tetrahidrofurano (THF)/agua; en el
sistema 2:8, se encontraron tamaños de partícula de 8.1 ± 0.2 nm para las Np´s
del copolímero PI y 9.0 ± 1.7 nm para las Np´s del copolímero PA.
Mediante un procedimiento rápido y sencillo, se logró la formación de los
nanocompositos (NC´s) de Np´s de plata (Ag) y las Np´s de los copolímeros. Se
analizó la morfología y la distribución de tamaño de las Np´s y los NC´s utilizando
la técnica de Microscopía Electrónica de Barrido de alta resolución (HR-SEM).
El NC formado por las Np´s esféricas de Ag y las Np´s del copolímero PA
conservó la morfología de ambos componentes y fue el sistema más estable. | es_MX |
| dc.description | ABSTRACT
This project describes the formation of silver nanoparticles (Np´s) with spherical
morphology of 12.7 ± 1.2 nm of diameter and triangular morphology with 28.9 ± 0.8
nm for each side of the triangles, also some nanotriangles with size less than 5 nm
were observed.
The stability of the Np´s was achieved using the dithiocarbamate (DTC): 4-
(ethylaminodithiocarbamate) methylpyridine di-n-butyltin (IV) with the concentration
of 8.69×10-3 mM. UV-vis optical analysis of Np´s showed a wavelength of 390 nm
characteristic to the spherical morphology and two signals 331 and 754 nm for the
triangular morphology, confirming thus each morphology. UV-vis spectra also
showed the stability of Np´s with DTC for more than three months.
Np´s of copolymers based in 3-hexylthiophene with 2-(ethyl(4-(4-
nitrostyryl)phenyl)amino)ethyl-2-(thiophen-3-yl)acetate (PI) and 3-hexylthiophene
with (E)-2-(ethyl(4-((4-nitrophenyl) diazenyl) phenyl) amino) ethyl 2-(thiophen-3-yl)
acetate (PA), were obtained in THF/water ratios; in system 2:8, a particle size of
8.1 ± 0.2 nm for Np's of copolymer PI and 9.0 ± 1.7 nm for Np's of the PA
copolymer were found.
By quick and easy procedure, the formation of nanocomposites (NC´s) of silver
(Ag) Np´s and copolymers Np´s was achieved. The morphology and size
distribution of the Np´s and NC´s was analyzed using the technique of high
resolution scanning electron microscopy (HR-SEM).
The NC formed by the spherical Ag Np's and PA copolymer Np's preserved the
morphology of both components and was the most stable system. | es_MX |
| dc.format | pdf - Adobe PDF | es_MX |
| dc.language | spa - Español | es_MX |
| dc.publisher | autor | es_MX |
| dc.rights | openAccess - Acceso Abierto | es_MX |
| dc.subject | 7 - INGENIERÍA Y TECNOLOGÍA | es_MX |
| dc.subject.other | 33 - CIENCIAS TECNOLÓGICAS | es_MX |
| dc.title | Nanopartículas de plata y nanopartículas de politiofenos: síntesis, caracterización, análisis de su estabilidad con ditiocarbamatos y formación de nanocompositos | es_MX |
| dc.type | doctoralThesis - Tesis de doctorado | es_MX |
| uaem.unidad | Centro de Investigación en Ingeniería y Ciencias Aplicadas (CIICAP) - Centro de Investigación en Ingeniería y Ciencias Aplicadas (CIICAP) | es_MX |
| uaem.programa | Doctorado en Ingeniería y Ciencias Aplicadas - Doctorado en Ingeniería y Ciencias Aplicadas | es_MX |
| dc.type.publication | acceptedVersion | es_MX |
| dc.audience | researchers - Investigadores | es_MX |