| dc.description | Resumen.
Esta investigación se enfoca al uso de materiales de desecho y naturales tales como:
PET (polietilentereftalato) y mucílago de nopal, como agregados que pueden
modificar favorablemente las propiedades electroquímicas y mecánicas del concreto.
Se elaboraron muestras con diferentes geometrías de PET: fibras largas (FL),
rectángulos (R), mezcla de fibra largas + rectángulos (F-R) y fibras cortas (FC). El
PET se agregó al concreto como sustituto parcial de la arena con una relación
PET/arena en volumen de: 3%/97%, 5%/95% y 8%/92%. En el caso del mucílago de
nopal, se diseñaron tres concentraciones cuya relación en peso nopal-agua fue de
1:1, 1:2 y 1:3, obtenidas por dos métodos de extracción diferentes. A partir de los
resultados de ambos agregados por separado se determinó el porcentaje y
geometrías óptimas de PET, así como la mejor concentración de mucílago de nopal
para evaluar su efecto combinado en el concreto. Para realizar el ensayo de
resistencia a la compresión (F´c) las muestras se curaron durante 28, 42 y 56 días.
Para las pruebas electroquímicas las muestras se colocaron en una solución de
cloruro de sodio al 3%, simulando un entorno marino. Durante 240 a 300 días todas
las muestras fueron evaluadas a través de diversas técnicas electroquímicas como:
potencial de media celda (H.C.P.), ruido electroquímico (E.N.), espectroscopía de
impedancia electroquímica (E.I.S.) y resistencia a la polarización lineal (L.P.R.). Se
observó una disminución en los valores de F´c con el incremento en porcentaje de
PET. Para el mucílago de nopal se observó el efecto retardante de este aditivo en el
fraguado del concreto, sin embargo a las 42 y 56 días de curado la concentración 1:3
superó el valor de F´c de la muestra control. Todas las muestras con agregados de
PET y mucílago de nopal, tanto juntos como por separados, alcanzaron valores de
potencial más nobles en comparación con la muestra control, así como los valores
más altos de resistencia de ruido (Rn), resistencia a la polarización (Rp) y del módulo
de la impedancia IZI. Se obtuvo un circuito equivalente formado por una resistencia,
asociada a la solución en los poros del concreto y dos constantes de tiempo,
relacionadas con la película pasiva y la doble capa. Se apreció el efecto favorable de
los (R), la mezcla de (FL-R) y las (FC) y el mucílago de nopal en los valores de rapidez
de corrosión (Icorr), pues mantienen el acero en el rango de corrosión de despreciable
a baja por un mayor período de exposición al medio agresivo. | es_MX |
| dc.description | Abstract.
This research was focused on the use of waste and natural materials such as: PET
(polyethylene terephthalate) and nopal mucilage, as aggregates that can favorably
modify the electrochemical and compressive strength properties of concrete. Samples
with different PET geometries were made: long fibers (FL), rectangles (R), long fiber
mix + rectangles (FL-R) and short fibers (FC). PET was added to concrete as a partial
substitute for sand with a PET/sand ratio in volume of: 3%/97%, 5%/95% and 8%/92%.
In the case of nopal mucilage, three concentrations were designed whose nopal-water
weight ratio was 1:1, 1:2 and 1:3, obtained by two different extraction methods. From
the results of both aggregates separately, the percentage and optimal geometries of
PET were determined, as well as the best concentration of nopal mucilage to assess
its combined effect on concrete. To perform the compression resistance (F 'c) test, the
samples were cured for 28, 42 and 56 days. In the case of electrochemical tests, the
samples were exposed to solution of 3% sodium chloride, simulating a marine
environment. During 240 to 300 days all samples were evaluated through various
electrochemical techniques such as: half-cell potential (H.C.P.), electrochemical noise
(E.N.), electrochemical impedance spectroscopy (E.I.S.) and linear polarization
resistance (L.P.R.). A decrease in F´c values was observed with the increase in
percentage of PET. For the nopal mucilage the retarding effect of this additive was
observed in the setting of the concrete, however, at 42 and 56 days after curing, the
1:3 concentration exceeded the value of F´c of the control sample. All samples with
aggregates of PET and nopal mucilage, both together and separately, reached more
noble potential values compared to the control sample, as well as higher values of
noise resistance (Rn), polarization resistance (Rp) and the impedance module IZI. An
equivalent circuit formed by a resistance, associated with the solution in the pores of
the concrete and two time constants, related to the passive film and the double layer
was obtained. The favorable effect of the (R), the mixture of (FL-R) and the (FC) and
the nopal mucilage in the values of corrosion rate (Icorr) was appreciated, since they
keep the steel in the negligible to low corrosion range for a longer exposure period to
the aggressive environment. | es_MX |
| dc.format | pdf - Adobe PDF | es_MX |
| dc.language | spa - Español | es_MX |
| dc.publisher | El autor | es_MX |
| dc.rights | openAccess - Acceso Abierto | es_MX |
| dc.subject | 7 - INGENIERÍA Y TECNOLOGÍA | es_MX |
| dc.subject.other | 33 - CIENCIAS TECNOLÓGICAS | es_MX |
| dc.title | Efecto del pet reciclado y del mucílago de nopal en las propiedades electroquímicas y mecánicas del concreto | es_MX |
| dc.type | doctoralThesis - Tesis de doctorado | es_MX |
| uaem.unidad | Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) - Instituto de Investigación en Ciencias Básicas y Aplicadas (IICBA) | es_MX |
| uaem.programa | Doctorado en Ingeniería y Ciencias Aplicadas - Doctorado en Ingeniería y Ciencias Aplicadas | es_MX |
| dc.type.publication | acceptedVersion | es_MX |
| dc.audience | researchers - Investigadores | es_MX |